ASTM A36 is the most commonly used mild and hot-rolled steel. It has excellent welding properties and is suitable for grinding, punching, tapping, drilling and machining processes. Yield strength of ASTM A36 is less than that of cold roll C1018, thus enabling ASTM A36 to bend more readily than C1018. Normally, larger diameters in ASTM A36 are not produced since C1018 hot roll rounds are used.
ASTM A36 steel plate is the most widely used hot-rolled steel product. As a kind of carbon structural steel product, its relative products are round rod steel, angle bar, and steel sections such as I-Beams, H-beams, angles, and channels. Hot rolled ASTM A36 has rough surface on the final product, it’s easy for further processing like machining.
Application:
| ASTM A36 Carbon Structural Steel Plate Application fields | |||||||
|---|---|---|---|---|---|---|---|
| machinery parts | frames | fixtures | bearing plates | tanks | bins | bearing plates | forgings |
| base plates | gears | cams | sprockets | jigs | rings | templates | fixtures |
| ASTM A36 Steel Plate Fabrication Options | |||||||
| cold bending | mild hot forming | punching | machining | welding | cold bending | mild hot forming | punching |
Chemical Composition:
ASTM A36 Hot Rolled Steel Plate | Chemical Compostion | |
|---|---|---|
| Element | content | |
| Carbon, C | 0.25 - 0.290 % | |
| Copper, Cu | 0.20 % | |
| Iron, Fe | 98.0 % | |
| Manganese, Mn | 1.03 % | |
| Phosphorous, P | 0.040 % | |
| Silicon, Si | 0.280 % | |
| Sulfur, S | 0.050 % | |
Physical Property:
| Physical Property | Metric | Imperial |
|---|---|---|
| Density | 7.85 g/cm3 | 0.284 lb/in3 |
Mechanical Property:
| ASTM A36 Hot Rolled Steel Plate | ||
|---|---|---|
| Mechanical Properties | Metric | Imperial |
| Tensile Strength, Ultimate | 400 - 550 MPa | 58000 - 79800 psi |
| Tensile Strength, Yield | 250 MPa | 36300 psi |
| Elongation at Break (in 200 mm) | 20.0 % | 20.0 % |
| Elongation at Break (in 50 mm) | 23.0 % | 23.0 % |
| Modulus of Elasticity | 200 GPa | 29000 ksi |
| Bulk Modulus (typical for steel) | 140 GPa | 20300 ksi |
| Poissons Ratio | 0.260 | 0.260 |
| Shear Modulus | 79.3 GPa | 11500 ksi |
bolted, riveted or welded construction of bridges, buildings and oil rigs. Used in forming tanks, bins, bearing plates, fixtures, rings, templates, jigs, sprockets, cams, gears, base plates, forgings, ornamental works, stakes, brackets, automotive and agricultural equipment, frames, machinery parts. It is also used for various parts obtained by flame cutting such as in parking garages, walkways, boat landing ramps and trenches.